Weld cracking in ferrous alloys:
Weld cracks are unacceptable defects that can compromise the integrity of welded structures. Weld cracking can lead to structural failures which at best will require remedial action and at worst can lead to loss of life. Weld cracking in ferrous alloys reviews the latest developments in the design,...
Gespeichert in:
| Format: | Elektronisch E-Book |
|---|---|
| Sprache: | English |
| Veröffentlicht: |
Cambridge, England
Woodhead Publishing Limited
2009
|
| Schriftenreihe: | Woodhead Publishing in materials
|
| Schlagworte: | |
| Online-Zugang: | FLA01 Volltext |
| Zusammenfassung: | Weld cracks are unacceptable defects that can compromise the integrity of welded structures. Weld cracking can lead to structural failures which at best will require remedial action and at worst can lead to loss of life. Weld cracking in ferrous alloys reviews the latest developments in the design, evaluation, prevention and repair of weld cracks. Part one reviews the fundamentals as well as recent advances in the areas of welding technology, design and material selection for preventing weld cracking. Part two analyses weld crack behaviour, evaluation and repair of cracking/cracked welds. The book benefits from an extensive and robust chapter on the topic of NDE and quality control that was contributed by one of the most respected non-destructive evaluation and development groups in the world. Part three covers environment assisted weld cracking. With its distinguished editor and international team of contributors, Weld cracking in ferrous alloys is a valuable source of reference for all those concerned with improving the quality of welding and welded components. In the planning and development of this book, particular care has been taken to make the chapters suitable for people from other disciplines who need to understand weld cracking and failure. Reviews the latest developments in the design, evaluation, prevention and repair of weld cracksAssesses recent advances in welding technology, design and material selectionAnalyses weld crack behaviour, evaluation and repair including environment assisted weld cracking |
| Beschreibung: | Includes bibliographical references and index |
| Beschreibung: | 1 online resource (581 pages) illustrations |
| ISBN: | 9781845695453 1845695453 |
Internformat
MARC
| LEADER | 00000nmm a2200000zc 4500 | ||
|---|---|---|---|
| 001 | BV046126471 | ||
| 003 | DE-604 | ||
| 005 | 00000000000000.0 | ||
| 007 | cr|uuu---uuuuu | ||
| 008 | 190827s2009 |||| o||u| ||||||eng d | ||
| 020 | |a 9781845695453 |9 978-1-84569-545-3 | ||
| 020 | |a 1845695453 |9 1-84569-545-3 | ||
| 035 | |a (ZDB-33-ESD)ocn874144223 | ||
| 035 | |a (OCoLC)874144223 | ||
| 035 | |a (DE-599)BVBBV046126471 | ||
| 040 | |a DE-604 |b ger |e rda | ||
| 041 | 0 | |a eng | |
| 082 | 0 | |a 581 |2 23 | |
| 245 | 1 | 0 | |a Weld cracking in ferrous alloys |c edited by Raman Singh |
| 264 | 1 | |a Cambridge, England |b Woodhead Publishing Limited |c 2009 | |
| 300 | |a 1 online resource (581 pages) |b illustrations | ||
| 336 | |b txt |2 rdacontent | ||
| 337 | |b c |2 rdamedia | ||
| 338 | |b cr |2 rdacarrier | ||
| 490 | 0 | |a Woodhead Publishing in materials | |
| 500 | |a Includes bibliographical references and index | ||
| 520 | |a Weld cracks are unacceptable defects that can compromise the integrity of welded structures. Weld cracking can lead to structural failures which at best will require remedial action and at worst can lead to loss of life. Weld cracking in ferrous alloys reviews the latest developments in the design, evaluation, prevention and repair of weld cracks. Part one reviews the fundamentals as well as recent advances in the areas of welding technology, design and material selection for preventing weld cracking. Part two analyses weld crack behaviour, evaluation and repair of cracking/cracked welds. The book benefits from an extensive and robust chapter on the topic of NDE and quality control that was contributed by one of the most respected non-destructive evaluation and development groups in the world. Part three covers environment assisted weld cracking. With its distinguished editor and international team of contributors, Weld cracking in ferrous alloys is a valuable source of reference for all those concerned with improving the quality of welding and welded components. In the planning and development of this book, particular care has been taken to make the chapters suitable for people from other disciplines who need to understand weld cracking and failure. Reviews the latest developments in the design, evaluation, prevention and repair of weld cracksAssesses recent advances in welding technology, design and material selectionAnalyses weld crack behaviour, evaluation and repair including environment assisted weld cracking | ||
| 650 | 7 | |a Welded joints / Cracking |2 fast | |
| 650 | 7 | |a Welded joints / Testing |2 fast | |
| 650 | 4 | |a Welded joints |x Testing | |
| 650 | 4 | |a Iron alloys |x Cracking | |
| 650 | 4 | |a Welded joints |x Cracking | |
| 700 | 1 | |a Singh, Raman |e Sonstige |4 oth | |
| 776 | 0 | 8 | |i Erscheint auch als |n Druck-Ausgabe |z 9781420079630 |
| 776 | 0 | 8 | |i Erscheint auch als |n Druck-Ausgabe |z 9781845693008 |
| 856 | 4 | 0 | |u http://www.sciencedirect.com/science/book/9781845693008 |x Verlag |z URL des Erstveröffentlichers |3 Volltext |
| 912 | |a ZDB-33-ESD | ||
| 999 | |a oai:aleph.bib-bvb.de:BVB01-031506924 | ||
| 966 | e | |u http://www.sciencedirect.com/science/book/9781845693008 |l FLA01 |p ZDB-33-ESD |q FLA_PDA_ESD |x Verlag |3 Volltext | |
Datensatz im Suchindex
| _version_ | 1804180446585552896 |
|---|---|
| any_adam_object | |
| building | Verbundindex |
| bvnumber | BV046126471 |
| collection | ZDB-33-ESD |
| ctrlnum | (ZDB-33-ESD)ocn874144223 (OCoLC)874144223 (DE-599)BVBBV046126471 |
| dewey-full | 581 |
| dewey-hundreds | 500 - Natural sciences and mathematics |
| dewey-ones | 581 - Specific topics in natural history of plants |
| dewey-raw | 581 |
| dewey-search | 581 |
| dewey-sort | 3581 |
| dewey-tens | 580 - Plants |
| discipline | Biologie |
| format | Electronic eBook |
| fullrecord | <?xml version="1.0" encoding="UTF-8"?><collection xmlns="http://www.loc.gov/MARC21/slim"><record><leader>03127nmm a2200433zc 4500</leader><controlfield tag="001">BV046126471</controlfield><controlfield tag="003">DE-604</controlfield><controlfield tag="005">00000000000000.0</controlfield><controlfield tag="007">cr|uuu---uuuuu</controlfield><controlfield tag="008">190827s2009 |||| o||u| ||||||eng d</controlfield><datafield tag="020" ind1=" " ind2=" "><subfield code="a">9781845695453</subfield><subfield code="9">978-1-84569-545-3</subfield></datafield><datafield tag="020" ind1=" " ind2=" "><subfield code="a">1845695453</subfield><subfield code="9">1-84569-545-3</subfield></datafield><datafield tag="035" ind1=" " ind2=" "><subfield code="a">(ZDB-33-ESD)ocn874144223</subfield></datafield><datafield tag="035" ind1=" " ind2=" "><subfield code="a">(OCoLC)874144223</subfield></datafield><datafield tag="035" ind1=" " ind2=" "><subfield code="a">(DE-599)BVBBV046126471</subfield></datafield><datafield tag="040" ind1=" " ind2=" "><subfield code="a">DE-604</subfield><subfield code="b">ger</subfield><subfield code="e">rda</subfield></datafield><datafield tag="041" ind1="0" ind2=" "><subfield code="a">eng</subfield></datafield><datafield tag="082" ind1="0" ind2=" "><subfield code="a">581</subfield><subfield code="2">23</subfield></datafield><datafield tag="245" ind1="1" ind2="0"><subfield code="a">Weld cracking in ferrous alloys</subfield><subfield code="c">edited by Raman Singh</subfield></datafield><datafield tag="264" ind1=" " ind2="1"><subfield code="a">Cambridge, England</subfield><subfield code="b">Woodhead Publishing Limited</subfield><subfield code="c">2009</subfield></datafield><datafield tag="300" ind1=" " ind2=" "><subfield code="a">1 online resource (581 pages)</subfield><subfield code="b">illustrations</subfield></datafield><datafield tag="336" ind1=" " ind2=" "><subfield code="b">txt</subfield><subfield code="2">rdacontent</subfield></datafield><datafield tag="337" ind1=" " ind2=" "><subfield code="b">c</subfield><subfield code="2">rdamedia</subfield></datafield><datafield tag="338" ind1=" " ind2=" "><subfield code="b">cr</subfield><subfield code="2">rdacarrier</subfield></datafield><datafield tag="490" ind1="0" ind2=" "><subfield code="a">Woodhead Publishing in materials</subfield></datafield><datafield tag="500" ind1=" " ind2=" "><subfield code="a">Includes bibliographical references and index</subfield></datafield><datafield tag="520" ind1=" " ind2=" "><subfield code="a">Weld cracks are unacceptable defects that can compromise the integrity of welded structures. Weld cracking can lead to structural failures which at best will require remedial action and at worst can lead to loss of life. Weld cracking in ferrous alloys reviews the latest developments in the design, evaluation, prevention and repair of weld cracks. Part one reviews the fundamentals as well as recent advances in the areas of welding technology, design and material selection for preventing weld cracking. Part two analyses weld crack behaviour, evaluation and repair of cracking/cracked welds. The book benefits from an extensive and robust chapter on the topic of NDE and quality control that was contributed by one of the most respected non-destructive evaluation and development groups in the world. Part three covers environment assisted weld cracking. With its distinguished editor and international team of contributors, Weld cracking in ferrous alloys is a valuable source of reference for all those concerned with improving the quality of welding and welded components. In the planning and development of this book, particular care has been taken to make the chapters suitable for people from other disciplines who need to understand weld cracking and failure. Reviews the latest developments in the design, evaluation, prevention and repair of weld cracksAssesses recent advances in welding technology, design and material selectionAnalyses weld crack behaviour, evaluation and repair including environment assisted weld cracking</subfield></datafield><datafield tag="650" ind1=" " ind2="7"><subfield code="a">Welded joints / Cracking</subfield><subfield code="2">fast</subfield></datafield><datafield tag="650" ind1=" " ind2="7"><subfield code="a">Welded joints / Testing</subfield><subfield code="2">fast</subfield></datafield><datafield tag="650" ind1=" " ind2="4"><subfield code="a">Welded joints</subfield><subfield code="x">Testing</subfield></datafield><datafield tag="650" ind1=" " ind2="4"><subfield code="a">Iron alloys</subfield><subfield code="x">Cracking</subfield></datafield><datafield tag="650" ind1=" " ind2="4"><subfield code="a">Welded joints</subfield><subfield code="x">Cracking</subfield></datafield><datafield tag="700" ind1="1" ind2=" "><subfield code="a">Singh, Raman</subfield><subfield code="e">Sonstige</subfield><subfield code="4">oth</subfield></datafield><datafield tag="776" ind1="0" ind2="8"><subfield code="i">Erscheint auch als</subfield><subfield code="n">Druck-Ausgabe</subfield><subfield code="z">9781420079630</subfield></datafield><datafield tag="776" ind1="0" ind2="8"><subfield code="i">Erscheint auch als</subfield><subfield code="n">Druck-Ausgabe</subfield><subfield code="z">9781845693008</subfield></datafield><datafield tag="856" ind1="4" ind2="0"><subfield code="u">http://www.sciencedirect.com/science/book/9781845693008</subfield><subfield code="x">Verlag</subfield><subfield code="z">URL des Erstveröffentlichers</subfield><subfield code="3">Volltext</subfield></datafield><datafield tag="912" ind1=" " ind2=" "><subfield code="a">ZDB-33-ESD</subfield></datafield><datafield tag="999" ind1=" " ind2=" "><subfield code="a">oai:aleph.bib-bvb.de:BVB01-031506924</subfield></datafield><datafield tag="966" ind1="e" ind2=" "><subfield code="u">http://www.sciencedirect.com/science/book/9781845693008</subfield><subfield code="l">FLA01</subfield><subfield code="p">ZDB-33-ESD</subfield><subfield code="q">FLA_PDA_ESD</subfield><subfield code="x">Verlag</subfield><subfield code="3">Volltext</subfield></datafield></record></collection> |
| id | DE-604.BV046126471 |
| illustrated | Illustrated |
| indexdate | 2024-07-10T08:35:54Z |
| institution | BVB |
| isbn | 9781845695453 1845695453 |
| language | English |
| oai_aleph_id | oai:aleph.bib-bvb.de:BVB01-031506924 |
| oclc_num | 874144223 |
| open_access_boolean | |
| physical | 1 online resource (581 pages) illustrations |
| psigel | ZDB-33-ESD ZDB-33-ESD FLA_PDA_ESD |
| publishDate | 2009 |
| publishDateSearch | 2009 |
| publishDateSort | 2009 |
| publisher | Woodhead Publishing Limited |
| record_format | marc |
| series2 | Woodhead Publishing in materials |
| spelling | Weld cracking in ferrous alloys edited by Raman Singh Cambridge, England Woodhead Publishing Limited 2009 1 online resource (581 pages) illustrations txt rdacontent c rdamedia cr rdacarrier Woodhead Publishing in materials Includes bibliographical references and index Weld cracks are unacceptable defects that can compromise the integrity of welded structures. Weld cracking can lead to structural failures which at best will require remedial action and at worst can lead to loss of life. Weld cracking in ferrous alloys reviews the latest developments in the design, evaluation, prevention and repair of weld cracks. Part one reviews the fundamentals as well as recent advances in the areas of welding technology, design and material selection for preventing weld cracking. Part two analyses weld crack behaviour, evaluation and repair of cracking/cracked welds. The book benefits from an extensive and robust chapter on the topic of NDE and quality control that was contributed by one of the most respected non-destructive evaluation and development groups in the world. Part three covers environment assisted weld cracking. With its distinguished editor and international team of contributors, Weld cracking in ferrous alloys is a valuable source of reference for all those concerned with improving the quality of welding and welded components. In the planning and development of this book, particular care has been taken to make the chapters suitable for people from other disciplines who need to understand weld cracking and failure. Reviews the latest developments in the design, evaluation, prevention and repair of weld cracksAssesses recent advances in welding technology, design and material selectionAnalyses weld crack behaviour, evaluation and repair including environment assisted weld cracking Welded joints / Cracking fast Welded joints / Testing fast Welded joints Testing Iron alloys Cracking Welded joints Cracking Singh, Raman Sonstige oth Erscheint auch als Druck-Ausgabe 9781420079630 Erscheint auch als Druck-Ausgabe 9781845693008 http://www.sciencedirect.com/science/book/9781845693008 Verlag URL des Erstveröffentlichers Volltext |
| spellingShingle | Weld cracking in ferrous alloys Welded joints / Cracking fast Welded joints / Testing fast Welded joints Testing Iron alloys Cracking Welded joints Cracking |
| title | Weld cracking in ferrous alloys |
| title_auth | Weld cracking in ferrous alloys |
| title_exact_search | Weld cracking in ferrous alloys |
| title_full | Weld cracking in ferrous alloys edited by Raman Singh |
| title_fullStr | Weld cracking in ferrous alloys edited by Raman Singh |
| title_full_unstemmed | Weld cracking in ferrous alloys edited by Raman Singh |
| title_short | Weld cracking in ferrous alloys |
| title_sort | weld cracking in ferrous alloys |
| topic | Welded joints / Cracking fast Welded joints / Testing fast Welded joints Testing Iron alloys Cracking Welded joints Cracking |
| topic_facet | Welded joints / Cracking Welded joints / Testing Welded joints Testing Iron alloys Cracking Welded joints Cracking |
| url | http://www.sciencedirect.com/science/book/9781845693008 |
| work_keys_str_mv | AT singhraman weldcrackinginferrousalloys |